ROGA 30mm 傳統戶外塑木地板在業內又被稱為第一代戶外塑木地板。傳統WPC 戶外塑木地板由木纖維和油基表面紋理製成。與最新的覆蓋(共擠)戶外塑木地板相比,第一代 WPC戶外塑木地板可以提供經濟的解決方案。
經 ASTM D792-13方法B的密度測試結果為 1.27 g/cm³ |
經 ASTM D790-10程序A的彎曲測試結果:彎曲強度為 30.2 MPa,彎曲模量為 2840 MP |
經 ASTM D4812-11懸臂梁無缺口衝擊強度測試結果為 90 J/m |
經 ASTM D2240-05(2010)肖氏硬度測試結果為 D/65/1 |
經 ASTM D638-14拉伸測試結果為 20.9 MPa |
經 ASTM D570-98(2010)ε1 吸水率測試結果為 0.43 % |
經 ASTM D696 – 08線熱膨脹係數測試結果為 (1/℃) -30℃~30℃:36.67×10¯⁶ |
具有2面不同飾面效果 – 拉絲面 / 坑紋面 |
具有成本效益 |
結構: 中空 |
規格: 145mm x 30mm x 2000mm (3.12 平方呎) |
ROGA 30mm Traditional WPC decking board is also known in the industry as 1st generation composite board. Traditional WPC decking board are made from wood fibers and oil-based surface textures. Compared to the latest Capped (Co-Extrusion) Decking, 1st generation WPC can be offer an economical solution.
Density test of ASTM D792-13 Method B result 1.27 g/cm³ |
Flexural test of ASTM D790-10 Procedure A result: flexural strength 30.2 MPa and flexural modulus 2840 MP |
Izod Unnotched Impact Strength test of ASTM D4812-11 result 90 J/m |
Shore Hardness test of ASTM D2240-05(2010) result D/65/1 |
Tensile test of ASTM D638-14 result 20.9 MPa |
Water Absorption test of ASTM D570-98(2010)ε1 result 0.43 % |
Coefficient of linear thermal expansion test of ASTM D696 – 08, result (1/℃) -30℃~30℃:36.67×10⁻⁶ |
Boards with 2 different finishes surface: Brushed Side / Grooved Side |
Cost-effective |
Structure: Hollow |
Dimension: 145mm x 30mm x 2000mm (3.12 ft2) |